Bozhong Metal Group’s W1.2312 are more and more popular at home and abroad which has low cost , high quality and convenient
Video
  • Description
  • Parameter
A prehardened mold steel (300 HB/32 HRC) with improved machinability

W1.2312 is a chromium – manganese – molybdenum grade designed for plastic mold industry. This grade is normaly delivered in a prehardened condition at a hardness level of 300HB/32HRC. The grade has a fully homogeneous martensite – bainite microstructure.W1.2312 grade has specific sulfur addition (0.060% typical) in order to increase strongly its machinability. Compared to W1.2311 grade, 30% increase in milling speed and 300% increase in drilling speed can be expected. At constant cutting speed, tool life is multiplied a least by 5 when replacing W1.2311 by W1.2312 grade. W1.2312 is not suitable for polishing requirements.

Standard
AFNOR: 40 CMD8S
DIN: 40 CrMnMoS 8.6
WERKSTOFF Nb: 1.2312
AISI: ≈ P20

Chemical Analysis
Typical values (weight%)
C S P max Si Mn Cr Mo
.4 .060 .012 .3 1.5 1.9 .2

Mechanical Properties
Hardness YS 0.2 UTS Elongation Reduction
of area
Elastic modulus
HB MPa ksi MPa ksi % Z% GPa ksi
Longitudinal
direction
300 850 123 1270 184 10 45 205 29745
Longitudinal
direction
300 820 119 990 144 9 40 205 29745

Delivery Conditions
Dimensional program
Thickness Width
20 – 120 mm
(.79″ – 4.7″)
1500 – 2500 mm
(59″ – 98.4″)
120 – 350 mm
(4.7″ – 14″)
1500 – 2100 mm
(49″ – 82.7″)