Nitronic 33/S24000/XM29 Stainless Steel
If you are planning to buy Nitronic 33 stainless steel, Nitronic 33 bar, Nitronic 33 pipe,Nitronic 33 sheet, Nitronic 33 fittings, Nitronic 33 flange ect, please feel free to contact Bozhong Group, equipped with productive factory, we are always at y
Video
  • Parameter
  • Application

Nitronic 33 is a nitrogen-strengthened austenitic stainless steel that combines high yield strength with excellent toughness and ductility. It’s magnetic permeability remains very low after severe cold working and at cryogenic temperatures.

The alloy is superior to 304 stainless in at least five specific areas: (1) Yield strength in the annealed condition is approximately twice that of 304, (2) it has excellent strength and ductility at cryogenic temperatures, (3)has better stress corrosion cracking resistance than 304, (4) low magnetic permeability is retained at cryogenic temperatures and after severe cold working and, (5) resistance to wear and galling is superior to the standard austenitic stainless steels.

The corrosion resistance of Nitronic 33 is superior to 409 and, in general, is nearly equal to 304. In weak acid solutions, the corrosion resistance of Nitronic 33 approaches that of 304. In more aggressive media Nitronic 33 is somewhat less resistance than 304.

Nitronic 33 is markedly more resistant than 304 and 304L to stress corrosion cracking in hot chloride solutions at lower stress levels. At higher stress levels (approx. 50 ksi and above) they are equal. Like most stainless steels, Nitronic 33 is prone to pitting and crevice corrosion in seawater and other aggressive environments, and should not be used under these conditions unless cathodically protected.

Although Nitronic 33 is considerably stronger than the conventional austenitic stainless steels, the same fabricating equipment and techniques can generally be used.



STANDARDS
INDUSTEEL TRADEMARKS UNS ASTM EURONORMS EN SUS
Nitronic 33 S24000 XM29 - -
CHEMICAL ANALYSIS (%WEIGHT)
C Cr Ni Mo N Others
< 0,080 18 2,5 - - Mn = 13

PROPERTIES
0,2 Y.S. - Rp 0,2min ASTM / EN 0,2 Y.S. - Rp 0,2(2)typical value UTS - Rm min ASTM / EN UTS - Rm(2)typical value EI-A(1)% PREN(4) HOMOLOGATIONS
MPa Ksi MPa Ksi MPa Ksi MPa Ksi Last revised
380 55 435 63 690 100 720 104 40 18

Applications

  • Cryogenic Service – tanks valves, piping, flanges, and structural supports
  • Abrasion/Wear Resistance – screens, racks, and wear plates
  • Electrical (low magnetic permeability) – conduit shielding, MRI scanner supports, fittings, underground transmission risers and pipe and electronic support members
  • Marine – mine sweeper components and perming piers
  • Nuclear – spent fuel casks (internal supports)
  • Process Equipment – heat exchangers, pressure vessels and piping where 304 is borderline with respect to stress corrosion cracking.

APPLICATIONS
CHEMICAL INDUSTRIES PROCESS INDUSTRIES WATER TREATMENT STORAGE & TRANSPORTATION
Nitric Acid Sulfuric Acid Polymer& otheracids Fertilisers Pulp& Paper Hydrome-tallurgy Seawater& desalination Freshwater &Tanks Waste Water Chemical Tanks Cryogenic Tanks Renewable

POWER GENERATION OIL & GAS CONSTRUCTION
Nuclear Pollution control Hydroelectric Renewable Off & Onshore & production Refining & Gas processing Petrochemical Architecture Bridges

For more technical details :
(1) Indicative typical values
(2) Indicative typical values for thickness 20 mm at RT for transverse direction
(3) Hardening 496°C (925°F), 4h, air cooling
(4) PREN = Cr + 3.3 Mo + 16N
(5) PRENW = Cr + 3.3(Mo + 0.5W) + 16N