2507/S32750 Stainless Steel
If you are planning to buy 2507 stainless steel, 2507 bar, 2507 pipe, 2507 sheet, 2507 fittings, 2507 flange ect, please feel free to contact Bozhong Group, equipped with productive factory, we are always at your service.
Video
  • Parameter
  • Application

General Properties

Duplex 2507 (UNS S32750) is a super duplex stainless steel with 25% chromium, 4% molybdenum, and 7% nickel designed for demanding applications which require exceptional strength and corrosion resistance, such as chemical process, petrochemical, and seawater equipment. The steel has excellent resistance to chloride stress corrosion cracking, high thermal conductivity, and a low coefficient of thermal expansion. The high chromium, molybdenum, and nickel levels provide excellent resistance to pitting, crevice, and general corrosion.


S32507 Duplex stainless steel material offered by Bozhong Group are of high quality.

Bar,Pipe,Sheet and Plate ect can be offered.

STANDARDS
INDUSTEEL TRADEMARKS UNS ASTM EURONORMS EN SUS
S32750 2507 1.4410
X2CrNiMoN25-7-4
-
CHEMICAL ANALYSIS (%WEIGHT)
C Cr Ni Mo N Others
< 0,030 25 7 3,5 0,27

Mechanical Properties:

Ultimate Tensile Strength, ksi 116 min.
0.2% Offset Yield Strength 0.2%, ksi 80 min.
0.1% Offset Yield Strength 0.2%, ksi 91 min.
Elongation in 2 inches, % 15 min.
Hardness Rockwell C 32 max.
Impact Energy, ft.-lbs. 74 min.


Physical Propertries

Density lb/in3 0.28
Modulus of Elasticity psi x 106 29
Coefficient of Thermal Expansion
68-212°F/°F
x10-6/°F 7.2
Thermal Conductivity Btu/h ft °F 8.7
Heat Capacity Btu/lb/°F 0.12
Electrical Resistivity W-in x 10-6 31.5


Corrosion Resistance

General Corrosion

1、high chromium and molybdenum content of 2507 makes it extremely resistant to uniform corrosion by organic acids like formic and acetic acid.

2、provides excellent resistance to inorganic acids, especially those containing chlorides.

3、 can be used in dilute hydrochloric acid.

4、Pitting need not be a risk in the zone below the borderline in this figure, but crevices must be avoided.


Intergranural Corrosion

1、Low carbon content greatly lowers the risk of carbide precipitation at the grain boundaries during heat treatment.

2、Is highly resistant to carbide-related intergranular corrosion.


Stress Corrosion Cracking

1、Duplex structure of 2507 provides excellent resistance to chloride stress corrosion cracking (SCC).

2、Superior to 2205 in corrosion resistance and strength.

3、2507 is especially useful in offshore oil and gas applications and in wells with either naturally high brine levels or where brine has been injected to enhance recovery.


Pitting Corrosion

1、Different testing methods can be used to establish the pitting resistance of steels in chloride-containing solutions.


Crevice Corrosion

1、Highly resistant to crevice corrosion.


Processing

Hot forming
2507 should be hot worked between 1875°F and 2250°F. This should be followed by a solution anneal at 1925°F minimum and a rapid air or water quench.


Cold Forming
Most of the common stainless steel forming methods can be used for cold working 2507. The alloy has a higher yield strength and lower ductility than the austenitic steels so fabricators may find that higher forming forces, increased radius of bending, and increased allowance for springback are necessary. Deep drawing, stretch forming, and similar processes are more difficult to perform on 2507 than on an austenitic stainless steel. When forming requires more than 10% cold deformation, a solution anneal and quench are recommended.


Heat Treatment
2507 should be solution annealed and quenched after either hot or cold forming. Solution annealing should be done at a minimum of 1925°F. Annealing should be followed immediately by a rapid air or water quench. To obtain maximum corrosion resistance, heat treated products should be pickled and rinsed.


Welding
2507 possesses good weldability and can be joined to itself or other materials by shielded metal arc welding (SMAW), gas tungsten arc welding (GTAW), plasma arc welding (PAW), flux cored wire (FCW), or submerged arc welding (SAW). 2507/P100 filler metal is suggested when welding 2507 because it will produce the appropriate duplex weld structure.

Preheating of 2507 is not necessary except to prevent condensation on cold metal. The interpass weld temperature should not exceed 300°F or the weld integrity can be adversely affected. The root should be shielded with argon or 90% N2/10% H2 purging gas for maximum corrosion resistance. The latter provides better corrosion resistance.


With wide experience and expertise, Bohzong Group is one of the leading 2507 s32750 1.4410 f53 manufacturers and suppliers. We have hundreds of high-qualified workers at your service. Please rest assured to get the competitive price 2507 s32750 1.4410 f53 for sale with us.

Applications

1、Oil and gas industry equipment

2、Offshore platforms, heat exchangers, process and service water systems, fire-fighting systems, injection and ballast water systems

3、Chemical process industries, heat exchangers, vessels, and piping

4、Desalination plants, high pressure RO-plant and seawater piping

5、Mechanical and structural components, high strength, corrosion-resistant parts

6、Power industry FGD systems, utility and industrial scrubber systems, absorber towers, ducting, and piping