15-5 PH /S15500 Sheet/Bar/Pipe
If you are planning to buy 15-5 PH stainless steel, 15-5 PH bar, 15-5 PH pipe, 15-5 PH sheet, 15-5 PH fittings, 15-5 PH flange ect, please feel free to contact Bozhong Group, equipped with productive factory, we are always at your service.
Video
  • Parameter
  • Application

Common Trade Names: 15-5 Stainless, 15-5 PH Age hardening martensitic stainless.

Available Product Forms: Pipe, tube, fitting, flange, sheet, strip, plate, round bar, flat bar, fastener, forging stock, hexagon and wire.


Specifications


UNS S15500, ASTM A 564, ASTM A 693, ASTM A 705, AMS 5659, AMS 5862, STD 2154, ASME SA 564, SA693, SA705, Other:  BAC 5439 Rev H Class A Type1, BMS7-240G Type 1, BSS7055 Rev A


Introduction

Stainless steel 15 – 5 PH, also known as XM-12 or UNS S15500, is a modification of 17-4 PH developed in the 1960s. It has a more refined microstructure obtained through the remelting process. This refined structure improves toughness of the material. UNS S15500 also has low temperature hardening, good fabrication properties and excellent corrosion resistance, which makes it suitable for many industries. It can be machined in the solution-annealed state or in final heat treat condition. The strength and ductility of UNS S15500 can be enhanced through heating the material at different temperatures.

UNS S15500 is a martensitic precipitation hardening type stainless steel. Martensitic stainless steels were designed to be corrosion resistant and hardened through heat treatment.


STANDARDS
INDUSTEEL TRADEMARKS UNS ASTM EURONORMS EN SUS
15-5 PH S15500 XM12 1.4545 -
CHEMICAL ANALYSIS (%WEIGHT)
C Cr Ni Mo N Others
0,030 15 4,5 - - Cu = 3.3 Nb = 0.3

Mechanical properties

The mechanical properties of Grade 15-5 PH stainless steel are displayed in the following table.

Properties Metric Imperial
Tensile Strength 1380 MPa 200000 psi
Yield Strength 1275 MPa 184900 psi
Modulus of Elasticity 200 GPa 29000 ksi
Elongation at Break 10% 10%
Hardness, Brinell 420 420
Hardness, Knoop 451 451
Hardness, Rockwell B 104 104
Hardness, Rockewell C 44.2 44.2
Hardness, Vickers 445 445
Charpy Impact 10 J 7.38 ft.lb


Manufacturing process

UNS S15500 can be machined under any of the attainable conditions. Firstly, the alloy is mildly formed in the overaged condition. It is then welded using welding techniques such as shielded fusion or resistance methods. The material is heat treated at 1038°C (1900°F) for 1/2 h, and then air cooled. This process is followed by hot-working the material and annealing at 1038°C (1900°F) for 1 h. Finally, the alloy can be cold-worked to improve its yield strength。

Applications

The following are some of the major applications of Grade 15-5 PH stainless steel:

1、Marine gas turbine compressor sections

2、Hallow shafts

3、Paper mill equipment

4、Engine parts

5、Aircraft components

6、Gears

7、Fittings and fasteners

8、Nuclear reactor components